PA6Nanometer composite material
PA6 product brand 】 【 3400 n
【 features 】
Unlike traditional inorganic filler modified PA6 material, PA6 nanocomposite material PA6 3400 n has low density, can obviously reduce products weight; Products have excellent mechanical properties, fluidity and good appearance.
【 application 】
Mainly used for automobile external function parts, mechanical parts and electronic electrical splice pieces.
The typical data 】
|
测试项目
|
测试方法
|
单位
|
测试数据
|
|
密度
|
GB/T 1033.1-2008
|
g/cm3
|
1.15
|
|
拉伸强度
|
GB/T 1040-2006
|
MPa
|
83
|
|
断裂伸长率
|
%
|
18.9
|
|
弯曲强度
|
GB/T 9314-2000
|
MPa
|
130
|
|
弯曲模量
|
MPa
|
2927
|
|
简支梁缺口冲击强度（室温）
|
GB/T 1043.1-2008
|
KJ/m2
|
6
|
|
（-30℃）
|
KJ/m2
|
5.7
|
|
熔融指数(230℃/2.16kg)
|
GB/T 3682.1-2000
|
g/10min
|
12.6
|
|
灰分
|
GB/T 9345.1-2008
|
%
|
1.6
|
Note: this is a product of typical data, for reference only, specific products may make targeted adjustment according to user requirements.
【 reference molding process
|
干燥温度
|
110℃
|
干燥时间
|
4-6h
|
|
注射成型温度
|
225℃~240℃
|
模具温度
|
70-80℃
|
【 packing stored 】
Paper-plastic composite packaging, 25 kg/bag; Please placed in dry, ventilated area, to avoid moisture and heat.