PP NANOCOMPOSITES
【Product name】 PP 9400NST
【Product features】
Unlike traditional inorganic filler modification of PP material, PP matrix nanocomposites PP 9400 NST not only has low density, can obviously reduce products weight; And the products have higher heat resistance and shock resistance performance.
【Application field】
Mainly used for automobile interior and exterior decoration products, such as the bumper.
【Typical data】
|
Test project
|
The test method
|
Unit
|
The test data
|
|
Appearance
|
visual
|
|
White particles
|
|
Density
|
GB/T 1033.1-2008
|
g/cm3
|
0.98
|
|
The ball indentation hardness
（H132/10）
|
GB/T 3398.1-2008
|
N/mm2
|
27
|
|
The tensile strength
|
GB/T 1040-2006
|
MPa
|
21
|
|
Elongation at break
|
%
|
468
|
|
The bending strength
|
GB/T 9314-2000
|
MPa
|
24
|
|
The bending strength
|
MPa
|
681
|
|
Beam notched impact strength
|
GB/T 1043.1-2008
|
KJ/m2
|
NB
|
|
D card heat
|
GB/T1633-2000
|
℃
|
126
|
|
Melt flow index （230℃/5kg）
|
GB/T 3682-2000
|
g/10min
|
17
|
|
ASH
|
GB/T 9345.1-2008
|
%
|
8
|
Note: this is a product of typical data, for reference only, specific products may make targeted adjustment according to user requirements.
【Refer to the molding process 】
|
The drying temperature
|
90℃
|
The drying time
|
2-4h
|
|
Injection molding temperature
|
200℃~210℃
|
Mold temperature
|
50-60℃
|
【Packaging stored 】
Paper-plastic composite packaging, 25 kg/bag; Please placed in dry, ventilated area, to avoid moisture and heat.